Structures by: León-Reina L.
Total: 32
?
La1.56O4.33Si
Journal of Materials Chemistry (2005) 15, 25 2489
a=9.77167(28)Å b=9.77167Å c=7.21223(21)Å
α=90.0° β=90.0° γ=120.0°
?
La1.33O4.33SiSr0.33
Journal of Materials Chemistry (2005) 15, 25 2489
a=9.7347(7)Å b=9.7347Å c=7.2531(6)Å
α=90.0° β=90.0° γ=120.0°
?
GeLa1.33O4.33Sr0.33
Journal of Materials Chemistry (2005) 15, 25 2489
a=9.9422(6)Å b=9.9422Å c=7.3358(4)Å
α=90.0° β=90.0° γ=120.0°
?
La1.56O4.35Si
Journal of Materials Chemistry (2005) 15, 25 2489
a=9.81164(32)Å b=9.81164Å c=7.23354(24)Å
α=90.0° β=90.0° γ=120.0°
GeLa1.33O4.33Sr0.33
GeLa1.33O4.33Sr0.33
Journal of Materials Chemistry (2005) 15, 25 2489
a=9.91268(12)Å b=9.91268Å c=7.31937(10)Å
α=90.0° β=90.0° γ=120.0°
La1.55O4.33Si
La1.55O4.33Si
Journal of Materials Chemistry (2005) 15, 25 2489
a=9.728(6)Å b=9.728Å c=7.190(4)Å
α=90.0° β=90.0° γ=120.0°
La1.33O4.33SiSr0.33
La1.33O4.33SiSr0.33
Journal of Materials Chemistry (2005) 15, 25 2489
a=9.71191(8)Å b=9.71191Å c=7.23956(7)Å
α=90.0° β=90.0° γ=120.0°
?
Ge0.5La1.56O4.33Si0.5
Journal of Materials Chemistry (2005) 15, 25 2489
a=9.8527(17)Å b=9.8527Å c=7.2714(13)Å
α=90.0° β=90.0° γ=120.0°
Ge0.5La1.56O4.33Si0.5
Ge0.5La1.56O4.33Si0.5
Journal of Materials Chemistry (2005) 15, 25 2489
a=9.8335(4)Å b=9.8335Å c=7.25285(32)Å
α=90.0° β=90.0° γ=120.0°
La1.59O4.38Si
La1.59O4.38Si
J. Mater. Chem. (2004) 14, 7 1142-1149
a=9.76655(18)Å b=9.76655Å c=7.20962(14)Å
α=90.0° β=90.0° γ=120.0°
?
La1.59O4.36Si
J. Mater. Chem. (2004) 14, 7 1142-1149
a=9.72566(4)Å b=9.72566Å c=7.18636(4)Å
α=90.0° β=90.0° γ=120.0°
?
La1.59O4.37Si
J. Mater. Chem. (2004) 14, 7 1142-1149
a=9.80882(20)Å b=9.80882Å c=7.23353(16)Å
α=90.0° β=90.0° γ=120.0°
?
GeLa1.6O4.45
J. Mater. Chem. (2004) 14, 7 1142-1149
a=9.93931(13)Å b=9.93931Å c=7.28485(10)Å
α=90.0° β=90.0° γ=120.0°
?
GeLa1.6O4.43
J. Mater. Chem. (2004) 14, 7 1142-1149
a=9.96580(19)Å b=9.9658Å c=7.31160(16)Å
α=90.0° β=90.0° γ=120.0°
?
GeLa1.6O4.41
J. Mater. Chem. (2004) 14, 7 1142-1149
a=10.00745(28)Å b=10.00745Å c=7.33341(22)Å
α=90.0° β=90.0° γ=120.0°
?
GeLa1.44O4.39Sr0.23
Dalton transactions (Cambridge, England : 2003) (2007) 20 2058-2064
a=9.8914(6)Å b=9.8914Å c=7.3184(5)Å
α=90.0° β=90.0° γ=120.0°
?
La4.32O13.13Si3Sr0.68
Dalton transactions (Cambridge, England : 2003) (2007) 20 2058-2064
a=9.69541(16)Å b=9.69541Å c=7.21843(12)Å
α=90.0° β=90.0° γ=120.0°
?
La1.55O4.33Si
Dalton transactions (Cambridge, England : 2003) (2007) 20 2058-2064
a=9.7158(5)Å b=9.7158Å c=7.1884(4)Å
α=90.0° β=90.0° γ=120.0°
?
GeLa1.44O4.39Sr0.23
Dalton transactions (Cambridge, England : 2003) (2007) 20 2058-2064
a=9.8914(6)Å b=9.8914Å c=7.3184(5)Å
α=90.0° β=90.0° γ=120.0°
?
La4.32O13.13Si3Sr0.68
Dalton transactions (Cambridge, England : 2003) (2007) 20 2058-2064
a=9.69541(16)Å b=9.69541Å c=7.21843(12)Å
α=90.0° β=90.0° γ=120.0°
?
La1.55O4.33Si
Dalton transactions (Cambridge, England : 2003) (2007) 20 2058-2064
a=9.7158(5)Å b=9.7158Å c=7.1884(4)Å
α=90.0° β=90.0° γ=120.0°
C8H43Ce3O40P4
C8H43Ce3O40P4
Chemistry of Materials (2012) 24, 19 3780
a=13.4033(5)Å b=26.6912(10)Å c=11.0963(5)Å
α=90.0° β=90.0° γ=90.0°
C8H28Gd3O32P4,4(H2O)
C8H28Gd3O32P4,4(H2O)
Chemistry of Materials (2012) 24, 19 3780
a=13.0433(2)Å b=25.7014(3)Å c=11.07570(10)Å
α=90.00° β=90.00° γ=90.00°
?
Ga0.25LaO2.39Ti0.25
Chemistry of Materials (2005) 17, 24 5989
a=7.96293(15)Å b=11.09998(23)Å c=11.8294(4)Å
α=90.0° β=109.689(4)° γ=90.0°
?
C8H43La3O40P4
Chemistry of Materials (2012) 24, 19 3780
a=13.36042(33)Å b=26.2820(8)Å c=11.26679(32)Å
α=90.0° β=90.0° γ=90.0°
C8H43La3O40P4
C8H43La3O40P4
Chemistry of Materials (2012) 24, 19 3780
a=13.4677(4)Å b=26.8557(5)Å c=11.1160(5)Å
α=90.0° β=90.0° γ=90.0°
?
Al0.04O4.98Si0.96Sr3
Chemistry of Materials (2008) 20, 5 2026
a=6.94270(14)Å b=6.9427Å c=10.79916(25)Å
α=90.0° β=90.0° γ=90.0°
?
O5SiSr3
Chemistry of Materials (2008) 20, 5 2026
a=6.951343(33)Å b=6.951343Å c=10.76111(6)Å
α=90.0° β=90.0° γ=90.0°
C24H21Ca2O23P3,5(H2O)
C24H21Ca2O23P3,5(H2O)
Journal of the American Chemical Society (2014) 136, 15 5731
a=23.112(4)Å b=6.9534(13)Å c=22.638(4)Å
α=90° β=90° γ=90°
?
C24Ca2O23P3
Journal of the American Chemical Society (2014) 136, 15 5731
a=23.0652(7)Å b=6.97311(10)Å c=22.4165(7)Å
α=90.0° β=91.540(4)° γ=90.0°